PTI粉尘灰灰尘ACFTD灰尘ISO 12103-1 A2 Fine Test
Dust A2粉 ISO 12103-1 A4 Coarse Test Dust A4粉 ISO 12103-1 A3 Medium Test Dust
A3粉MTD粉尘 Arizona Test Dust Fractions 亚利桑那试验粉尘MIL 810E4 Silica Sand & Dust
Iron Oxide 波特兰水泥 Type IGlass Beads 玻璃珠 PV 树脂(喷融树脂) 汽车安全带测试粉尘ECE R16, Section 7.6.3.2 (GB 14166, Section 5.6.3.2液SoftC-2A Quartzose Mineral Dust DMT emission test dust (IEC 60312
5.1.2.5) Test Dust Type 8® DMT test dust type 8 (IEC 60312 5.1.2.3)
Quartzose Mineral DMT carpet test dust (IEC 60312 5.1.2.2) DMT Dolomite Sand (IEC 60312 5.1.2.1)A2 ISO 细灰 A4粗灰
亚利桑那沙子亚利桑那试验粉尘 美国ISO MTD粉尘A2测试粉A3中级试验粉尘AC DUST A2 粉尘 ISO 试验粉尘 亚力桑那A2粉尘
美国PTI碳黑粉尘 ISO 12103-2 M2铝粉 A2 ISO 细灰 ISO 12103-2 M3铝粉 ISO 12103-2 M4铝粉ISO
12103-2 M5铝粉JIS CLASS 2级粉尘 PTI 粉尘Nominal 0-5 Arizona Test Dust PTI 粉尘Nominal
10-20 Arizona Test Dust PTI 粗粉 PTI 粉尘Nominal 20-40 Arizona Test Dust
试验用粉尘12103-1 A2类粗粉粗灰美国亚利桑那A1粉 FLY ASH 飞灰Portland Cement波特兰水泥美国亚利桑那M5粉APPIE JIS
Z 8901 CLASS 1 试验粉尘APPIE JIS试验用粉体1 8种APPIE关东粉APPIE JIS test powders 1 class8
日本粉体工业技术协会APPIE APPIE JIS Z 8901 试验用粉体1,CLASS 8 APPIE JIS Z 8901 CLASS
15粉尘COTTON LINTERS 棉花纤维铁粉(赤)氧化铁 Carbon Black炭黑Ashrae test dust with carbon
black 試験用粉体1の7種, 8種, 11種JIS粉尘是依据JIS(Japanese Industrial
Standard,即日本工业标准)生产的试验粉尘,常被用于一些日系产品的检测。本公司可为广大国内用户提供日本进口的下述检测杂质,包括JIS Z
8901的试验粉尘和玻璃珠产品;请在与我们联系的时候描述清楚您需要的是下面哪种产品Quartz sand Talc Fly ash KANTO
(Japanese) loam Carbon black Calcium- carbonate (heavy) Glass beads GBL type
Glass beads GBM type White fused alu mina JIS Z8901 1 种(硅砂) JIS Z8901 3 种(硅砂)JIS
Z8901 4 种(滑石粉)JIS Z8901 7 种(关东粉)JIS Z8901 8
种(关东粉)铁粉0-5微米Fe3O4铁粉(赤)0-5微米Fe2O3
铁粉(赤)5-10微米Fe2O3 棉花纤维COTTON LINTERS
美国亚利桑那试验粉尘#IEC 60312试验粉尘#ISO 12103试验粉尘 周经理 ,韩国ITC沙尘试验箱
我司代理的美国PTI试验粉尘应用在包括滤清器行业,电子行业等;德国DMT试验粉尘对于房屋通风系统过滤器应用比较广泛;而日本JIS试验粉尘的也应用在滤清器行业和电子行业;下表列出了来自美国PTI公司 网站的常用的滤清器行业检测标准;
自从我司2007年七月取得美国PTI公司ZG代理权后。我们发现大部分客户并非来自滤清器行业,如果您已购买过我司代理的各种试验杂质,并愿意共享你们的标准,非常欢迎您来信联系我们,提供您使用的标准号,标准名称,对应的试验杂质以及简单的注释。我们将不断地扩充下表;
共享是件很棒的事!
Filtration Standards,
&
Specifications
|
Contaminants
Required
|
Comments &
|
Particle size distribution of
Class 1, Class 2 and Class 3
( Quartz sand )
|
Particle
size µm
|
Oversize(on mass basis)%
|
Class 1
|
Class 2
|
Class 3
|
5
|
-
|
88±5
|
61±3
|
10
|
-
|
76±3
|
43±3
|
20
|
-
|
62±3
|
27±3
|
30
|
-
|
50±3
|
15±3
|
40
|
-
|
39±3
|
9±3
|
45
|
99 min.
|
-
|
-
|
75
|
90±3
|
20max.
|
3max.
|
106
|
80±3
|
-
|
-
|
150
|
65±3
|
-
|
-
|
212
|
45±3
|
-
|
-
|
300
|
1max.
|
-
|
-
|
| |
Particle size distribution of
Class 4 and Class 9
( Talc )
|
|
*
|
Particle size distributions are defined by JIS Z 8901.
|
**
|
Sintered at 800°C, 2hours.
|
Note :1)
|
Class15 Mixed powder is distributed by Japan Air Cleaning Association and contains 72% of Class8, 23% of Class12 and 5% of cotton linter.
|
2)
|
Class13 and Class 14 are now absent ones.
|
*Particle size distribution of Test Powders 1
|
Particle size distribution of
Class 1, Class 2 and Class 3
( Quartz sand )
|
Particle
size µm
|
Oversize(on mass basis)%
|
Class 1
|
Class 2
|
Class 3
|
5
|
-
|
88±5
|
61±3
|
10
|
-
|
76±3
|
43±3
|
20
|
-
|
62±3
|
27±3
|
30
|
-
|
50±3
|
15±3
|
40
|
-
|
39±3
|
9±3
|
45
|
99 min.
|
-
|
-
|
75
|
90±3
|
20max.
|
3max.
|
106
|
80±3
|
-
|
-
|
150
|
65±3
|
-
|
-
|
212
|
45±3
|
-
|
-
|
300
|
1max.
|
-
|
-
|
|

|
Particle size distribution of
Class 4 and Class 9
( Talc )
|
|
Glass beads GBL type
|
Material used : Soda lime-silicate glass
Particle density : 2.1 to 2.5 g/cm3
Refractive index : 1.51 to 1.53
|
Particle size distribution
|
( Unit :µm ) ( % mass basis )
|
Class
|
Particle size in
case of 90% oversize
|
Particle size in
case of 50% oversize
|
Particle size in
case of 10% oversize
|
GBL-30
|
26 min.
|
30 ± 1.0
|
34 max.
|
GBL-40
|
37 min.
|
40 ± 1.0
|
45 max.
|
GBL-60
|
55 min.
|
59 ± 1.0
|
63 max.
|
GBL-100
|
95 min.
|
100 ± 1.0
|
105 max.
|

|
Glass beads GBM type
|
Material used : Barium-titanate glass
Particle density : 4.0 to 4.2 g/cm3
Refractive index : 1.92 to 1.94
|
Particle size distribution
|
( Unit :µm ) ( % mass basis )
|
Class
|
Particle size in
case of 90% oversize
|
Particle size in
case of 50% oversize
|
Particle size in
case of 10% oversize
|
GBM-20
|
18 min.
|
22 ± 1.0
|
26 max.
|
GBM-30
|
26 min.
|
30 ± 1.0
|
34 max.
|
GBM-40
|
37 min.
|
40 ± 1.0
|
45 max.
|

|
White fused alu mina
|
Material used : Al2O3 99% min.
Particle density : 3.9 to 4.0 g/cm3
|
Particle size distribution
|
( Unit :µm ) ( % mass basis )
|
Class
|
Particle size in
case of 94% oversize
|
Particle size in
case of 50% oversize
|
Particle size in
case of 3% oversize
|
No.1
|
0.8 min.
|
2 ± 0.5
|
5 max.
|
No.2
|
2.0 min.
|
4 ± 0.5
|
11 max.
|
No.3
|
4.5 min.
|
8 ± 0.6
|
20 max.
|
No.4
|
9.0 min.
|
14 ± 1
|
31 max.
|
No.5
|
20 min.
|
30 ± 2
|
58 max.
|
No.6
|
40 min.
|
57 ± 3
|
103 max.
|
|
|