SH-90 台湾可程式耐腐蚀试验箱

台湾可程式耐腐蚀试验箱

台湾可程式耐腐蚀试验箱 其余产品规格
规格型号          实验空间（W*D*H）      外箱尺寸（W*D*H）
SH-60             600*450*400mm          1075*630*1100mm
SH-90             900*600*500mm          1415*885*1285mm
SH-120           1200*1000*500mm         1900*1200*1400mm
SH-160           1600*1000*500mm         2300*1200*1400mm
SH-200           2000*1000*500mm         2700*1200*1400mm

可根据客户特别要求，订制非标产品。

三 Z大耗电量：AC 220V 单相3KW 50/60HZ

四 试验温度：
依CNS JIS ASTM GB2423.19规格，可设定式恒温控制
A  盐水喷雾试验：NSS，ACSS
1、试验室：35℃ ± 1℃
2、饱和空气桶：47℃±1℃
B  耐腐蚀试验：CASS（醋酸铜）
1、试验室：50℃ ± 1℃
2、饱和空气桶：63℃ ± 1℃

材质：
a、试验室採用P.V.C聚氯乙稀板，耐高温
b、试验室密封盖採用PVC耐衝击板
c、试药补充瓶採用隐藏式附水位表，清洗容易，不易破裂（气压缸自动开闭）
d、饱和空气桶採用SUS#304不銹钢耐高压桶保温效果Z佳
e、试验室盖架採平面分度架，可任意调整角度，四面落雾及受雾方面完全*，试药片放置数量多
 

ISO 9227-2006 人工气候腐蚀试验 盐雾试验

  The main task of technical committees is to prepare International Standards. Draft International Standards adopted by the technical committees are circulated to the member bodies for voting. Publication as an International Standard requires approval by at least 75% of the member bodies casting a vote.

  Attention is drawn to the possibility that some of the elements of this document may be the subject of patent rights.ISO shall not be held responsible for identifying any or all such patent rights.

  ISO 9227 was prepared by Technical Committee ISO/TC 156,Corrosion of metals and alloys,in collaboration with ISO/TC 35,Paints and vamishes,Subcommittee SC 9, General test methods for paints and vamishes, and ISO/TC 107,Metallic and other inorganic coatings, Subcommittee SC 7, Corrosion tests.

  This second edition cancels and replaces the first edition （ISO 9227:1990） and ISO 7253:1996, which have been technically revised.

  Introduction
  There is seldom a direct relation between resistance to the action of salt spray and resistance to corrosion in other media, because several factors influencing the progress of corrosion, such as the formation of protective films, vary greatly with the conditions encountered. Therefore, the test results should not be regarded as a direct guide to the corrosion resistance of the tested metallic materials, in all environments where these materials may be used. Also, the performance of different materials, during the test should not be taken as a direct guide to the corrosion resistance of these materials in service.