12642-14 Two Part Conductive Silver Paint导电银..._详细资料

产品信息

品牌其他品牌供货周期一个月应用领域医疗/卫生,化学品检测,生物产业,石油/化工

Two Part Conductive Silver Paint
两组分导电银胶

广泛应用在导电器件的无焊连接，比如电镜室的样本粘接，电子模型设计、电路板修复、表面导电连接、放电、屏蔽和接地等方面。室温凝固时间大约为10分钟。
12642-14
Two Part Conductive Silver Paint
14g
Composite Properties:
Material
Electrically conductive silver epoxy
Thinner
Do not thin
Color/Material
Part A: Bright silver epoxy Part B: Gray silver hardener
Cured Properties:
Volume Resistivity
<0.001 ohm-cm
Thermal Conductivity
11.0 BTU （in/F² hr°F）
Moisture resistance
Good
Temperature Range
-131 to 212° F （-55 to 100°C）
Cured Flexibility
Fair
Adhesion
Excellent
Typical Thickness
5 mil
Chemical resistance
Excellent
Lap shear
>1200 lbs （544 kg force）
Shore hardness
>70
Use Procedures:
Mix Ratio & Application
Mix equal amounts （1:1） by weight or volume. Non-critical. Mix thoroughly and apply to clean surface within 10 minutes.
Cure:
Curing times and overall conductivity depend primarily on temperature.
For fastest curing times, maximum conductivity and adhesion, heat the bond to between 150-250°F （65-121°C） for 5-10 minutes and allow to cool
Room temperature curing is possible in four hours at above 75°F（24°C）. For heating use a heat gun, hair dryer or oven. Curing at room temperature below 75°F（24°C） will result in longer curing times and increased overall cured resistance.
Maximum properties are achieved in twenty four hours.
Pot life
10 minutes @ 75°F （24°C）. Apply within 10 minutes of mixing.
Clean Up
Use a solvent before materials is fully cured.
Shelf Life
Twelve months unmixed and unopened.

您可能感兴趣的产品

12642-14 Two Part Conductive Silver Paint导电银...

产品信息

联系我们

关注我们

Material	Electrically conductive silver epoxy
Thinner	Do not thin
Color/Material	Part A: Bright silver epoxy Part B: Gray silver hardener

Volume Resistivity	<0.001 ohm-cm
Thermal Conductivity	11.0 BTU （in/F² hr°F）
Moisture resistance	Good
Temperature Range	-131 to 212° F （-55 to 100°C）
Cured Flexibility	Fair
Adhesion	Excellent
Typical Thickness	5 mil
Chemical resistance	Excellent
Lap shear	>1200 lbs （544 kg force）
Shore hardness	>70

Mix Ratio & Application	Mix equal amounts （1:1） by weight or volume. Non-critical. Mix thoroughly and apply to clean surface within 10 minutes.
Cure:	Curing times and overall conductivity depend primarily on temperature. For fastest curing times, maximum conductivity and adhesion, heat the bond to between 150-250°F （65-121°C） for 5-10 minutes and allow to cool Room temperature curing is possible in four hours at above 75°F（24°C）. For heating use a heat gun, hair dryer or oven. Curing at room temperature below 75°F（24°C） will result in longer curing times and increased overall cured resistance. Maximum properties are achieved in twenty four hours.
Pot life	10 minutes @ 75°F （24°C）. Apply within 10 minutes of mixing.
Clean Up	Use a solvent before materials is fully cured.
Shelf Life	Twelve months unmixed and unopened.